China JT Metal is the supplier of P20 tool steel round bar, flat bar and plate. Diameters in P20 can be sawn to your required lengths as one offs or multiple cut pieces. Rectangular pieces can be sawn from flat bar or plate to your specific sizes. P20 ground tool steel bar can be supplied, providing a quality precision ground bar to tight tolerances.

Contact our experienced sales team who will assist you with your P20 tool steel enquiry.

P20 tool steel is ideally suited for the production of plastic moulds. Typical applications include die holders, zinc die casting dies, backers, bolsters and injection moulds. The versatility of P20 tool steel with its high tensile characteristics enables uses for a variety of other applications such as shafts, rails and wear strips

Heat slowly, allowing sufficient time for the steel to become heated through. Begin forging at 1050°C. Do not forge below 930°C reheating if necessary. After forging, cool very slowly.

Heat uniformly to 770-790°C.  Soak well, cool slowly in the furnace.

When dies are heavily machined, we recommend stabilising just before finish machining in order to relieve machining strains. Heat to 460-500°C. Soak well and allow to cool in the air.

Heat the steel uniformly to 820-840°C until heated through. Quench in oil.

Heat uniformly and soak at the tempering temperature for at least one hour per 25mm of section. Allow to cool in still air.

The steel may be nitrided to give a wear resistant case of approximately Rockwell C60 surface hardness with a case depth of 0.35mm to 0.5mm. Nitriding P20 tool steel also increases the corrosion resistance. After nitriding at 525°C in ammonia gas the surface hardness of the P20 will be approximately 650HV.

Tools produced from may be case hardened, which can achieve a surface hardness of 55 to 59 HRc.

At 570ºC tufftriding of P20 tool steel will give a surface hardness of approximately 700HV. Allowing two hours treatment the surface hard layer will be approximately 0.1mm.

To avoid hydrogen embrittlement P20 should be tempered for 4 hours at 180°C for 4 hours after hard chromium plating.

Flame or induction hardening of P20 will achieve a hardness of 50 to 55HRc. Air cooling is preferable, though smaller components may require forced cooling. Temper immediately after hardening.

Heat treatment temperatures, including rate of heating, cooling and soaking times will vary due to factors such as the shape and size of each P20 steel component. Other considerations during the heat treatment process include the type of furnace, quenching medium and work piece transfer facilities. Please consult your heat treatment provider for full guidance on heat treatment of P20 tool steel.

P20 tool steel is supplied in accordance with our ISO 9001 : 2008 registration.

Contact China JT Metal with your enquiries for flat bar, square bar and round bar in P20 tool steel.